NILENE® P K40T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nt7r5I_NILENE-P-K40T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer 40% talcum filled flame rating UL94 HB. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.90 | % | Internal method |
| Flow direction | 0.90 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 31.0 | MPa | ISO 527-2/50 |
| Fracture | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.5 | % | ISO 527-2/50 |
| Fracture | 25 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 20 | J/m | ASTM D256 |
| 23°C | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 95.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(600°C) | 40 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 38GFRH300 | AD majoris | PBT | MALAT |
| Sylvin 8336-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Taitalac® 1003 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| EnCom PC/PBT 1013UV | EnCom, Inc. | PC+PBT | EnCom |
| Sylvin 9933-75 Red 6313 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |