Arak LLDPE LL0209AA / LL0209KJ
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Shazand (Arak) Petrochemical Corporation |
| Trademark: | Arak LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NsSkqR_Arak-LLDPE-LL0209AA-LL0209KJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL0209AA & LL0209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. LL0209AA & LL0209KJ are suitable for general purpose films, neat or in lean blends with LDPE and other ethylene polymers. Lean blends applications include sacks of all types, FFS and agricultural films. In lean blends they offer the following advantages:
LL0209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. LL0209AA & LL0209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight. Recommended melt temperature for extrusion is about 180°C - 225°C. * LL0209AA & LL0209KJ are suitable for food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D2838 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Thickness - Recommended / Available | 35-100 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 10.5 | MPa | |
| TD : Yield | 11.0 | MPa | |
| MD : Break | 41.0 | MPa | |
| TD : Break | 32.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 620 | % | |
| TD : Break | 840 | % | |
| Dart Drop Impact | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 150 | g | |
| TD : 25 µm | 370 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 56 | ASTM D2457 | |
| Haze | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 50.0 | °C | |
| Melt Temperature | 180 to 225 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A12^ F30 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Vi-Chem PVC V142-90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| NOVALAC FM 4029FN | Vyncolit N.V. | Phenolic | NOVALAC |
| EvoSource™ ABS 4136 | MBA Polymers | ABS | EvoSource™ |
| Elastamax™ XL-2075 | PolyOne Corporation | TPO (POE) | Elastamax™ |