Vyncolit® TX10916/5
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nrhg2c_VyncolitTX109165.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® TX10916/5 is a graphite filled phenolic molding compound with very good dimensional stability and a low coefficient of friction. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Apparent Density | 0.86 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.43 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Post Shrinkage | 0.090 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.63 | % | ISO 178 |
| Tensile Modulus | 18000 | MPa | ISO 527-2 |
| Tensile Stress | 56.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.38 | % | ISO 527-2 |
| Flexural Modulus | 16000 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Compressive Stress | 166 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 3.6 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 175 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.4E-5 | cm/cm/°C | TMA |
| Lateral | 3.2E-5 | cm/cm/°C | TMA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2500 A HB | RTP Company | PC+ABS | RTP |
| Monprene® OM-16260-02 | Teknor Apex Company | TPE | Monprene® |
| Vi-Chem PVC V150-70 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Abstron IMG 1120 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| TECACOMP® PA66 TC black 4028 | Ensinger GmbH | Nylon 66 | TECACOMP® |