DOWLEX™ IP 41
| Category: | HDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NqIXQL_DOWLEX-IP-41.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
DOWLEX™ IP 41 Polyethylene Resin is an Improved Processing high density resin designed to offer excellent processability and rigidity for food containers, overcaps and other general purpose applications. DOWLEX IP 41 resin balances peak molecular weight with a proprietary, optimized molecular weight distribution and a slightly higher density for excellent rigidity. This resin has demonstrated excellent processability over a wide range of processing conditions. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.956 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 42 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 29.0 | MPa | ASTM D638 |
| Fracture | 29.6 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 10 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1120 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 63.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 129 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 118 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Polyester TC 197 | Saudi Basic Industries Corporation (SABIC) | PET | SABIC® HDPE |
| Nylene® NX1170 | Custom Resins Group | Nylon 6 | Nylene® |
| AKROMID® A3 GF 15 black (2425) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Geon™ Vinyl Rigid Molding M5730 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| HiFill® PA6 0254 C | Techmer Engineered Solutions | Nylon 6 | HiFill® |