Mecoline IS RDX 5239 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NnfC5g_Mecoline-IS-RDX-5239-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compounds results in an extremely smooth surface, while still showing an extrudability at high speeds. The high temperature rating makes this compound an ideal choice for the insulation of heat-resistant wires and cables for applications in areas where wires and cables should withstand the high temperatures in small compartments. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 3.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 43 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 1 | > 16.0 | MPa | |
| -- 2 | > 8.00 | MPa | |
| Tensile Strain | |||
| Break 3 | > 300 | % | IEC 811-1-1 |
| Break 4 | > 500 | % | IEC 811-1-1 |
| Break, -50°C | > 30 | % | IEC 811-1-4 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 5 | IEC 540 | ||
| Elongation under load | 40 | % | |
| Residual elongation | < 10 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 155 to 165 | °C | |
| Extruder Screw L/D Ratio | >24.0:1.0 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | kV/mm | EN 60243-1 |
| Dielectric Constant (50 Hz) | 2.80 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 27 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 130 to 140 | °C | |
| Cylinder Zone 2 Temp. | 140 to 150 | °C | |
| Cylinder Zone 3 Temp. | 150 to 160 | °C | |
| Cylinder Zone 4 Temp. | 155 to 165 | °C | |
| Cylinder Zone 5 Temp. | 155 to 165 | °C | |
| Adapter Temperature | 155 to 165 | °C | |
| Die Temperature | 160 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | After crosslinking |
| 2 . | Before crosslinking |
| 3 . | After crosslinking |
| 4 . | Before crosslinking |
| 5 . | at 200°C/15min/0.2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4003 A | RTP Company | PPA | RTP |
| UNIBRITE® UA-1200 | Nippon A&L Inc. | ASA | UNIBRITE® |
| KOPLA PA66 KDE1010 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Idemitsu PS SEHI-112 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| HIPOLEN P® FL 5 | Hipol a.d. | PP Homopolymer | HIPOLEN P® |