Order Products : sales@su-jiao.com
Monprene® SP-13064
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nm6qc7_Monprene-SP-13064.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®SP-13064 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 66 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 64 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 2.49 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 3.52 | MPa | ASTM D412 |
| 300% strain 3 | 4.48 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 5.58 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 12.7 | MPa | ASTM D412 |
| Flow : Fracture | 10.0 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 590 | % | ASTM D412 |
| Flow : Fracture | 570 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 52.5 | kN/m | ASTM D624 |
| Flow | 44.5 | kN/m | ASTM D624 |
| Compression Set 8(23°C, 22 hr) | 15 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 232 | °C | |
| Middle Temperature | 188 - 238 | °C | |
| Front Temperature | 193 - 243 | °C | |
| Nozzle Temperature | 199 - 249 | °C | |
| Processing (Melt) Temp | 199 - 249 | °C | |
| Mold Temperature | 10.0 - 32.2 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 182 - 232 | °C | |
| Cylinder Zone 2 Temp. | 188 - 238 | °C | |
| Cylinder Zone 3 Temp. | 193 - 243 | °C | |
| Cylinder Zone 5 Temp. | 199 - 249 | °C | |
| Die Temperature | 199 - 249 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 1060 | RTP Company | PBT | RTP |
| RheTech Thermoplastic Polyolefin FT4700-01A | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Trexprene® A70BWEB-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| HANWHA CP-705 | Hanwha Chemical | PVC Copolymer | HANWHA |
| EPLAMID 66 GX0 25 RP | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |