KEBAFORM® C 906 LF
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BARLOG plastics GmbH |
| Trademark: | KEBAFORM® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NlVTc0_KEBAFORM-C-906-LF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM Copolymer unreinforced, improved wear and friction |
| General Information | |
|---|---|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 2.0 | % | |
| Flow | 2.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.21 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2150 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 53.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.3E-4 | cm/cm/°C | |
| Transverse | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPH-20G Black | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| EVALENE® PP PHJ1201 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| HiFill® PA6/6 GF15 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Polifil® Nylon 71MR | The Plastics Group | Nylon 66 | Polifil® Nylon |
| Sylvin 8200-60UV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |