4MID® 9A22130 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | 4Plas |
| Trademark: | 4MID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NkYQ1x_4MID-9A22130-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4MID 9A22130 H is a Standard Flow 30% Glass Fibre Reinforced Heat Stabilised PA66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction | 1.1 | % | |
| Flow direction | 0.30 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 1.9 | % | ISO 62 |
| Moisture Content | < 2000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 190 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 11 | kJ/m² | ISO 180/1A |
| 23°C | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 70 | kJ/m² | ISO 180/1U |
| 23°C | 80 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 255 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 255 | °C | ISO 306/B |
| Melting Temperature 2 | 262 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 90 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | IEC 60250 | |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 70.0 - 110 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M40053 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| STERalloy™ FDG 2036 | Hapco Inc. | TP, Unspecified | STERalloy™ FDG |
| DOMAMID® 6G30H | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| LNP™ COLORCOMP™ D10006U compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| MAXATEL® AC90TFSi-BK | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |