EPLAMID 66 GFS 40 HS NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NhQPqE_EPLAMID-66-GFS-40-HS-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66, reinforced with 40% of glass fiber, heat stabilized, lubricated for injection moulding. Eplamid 66 GFS 40 HS is used in all sectors of industry, offering a perfect balance of thermal and mechanical properties. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.44 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 0.40 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.20 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 40 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 90 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 13000 | 12500 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 220 | 210 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 2.0 | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 12700 | 12400 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 280 | 250 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 16 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 254 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 255 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUPLENE® R520F | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Fiberfil® PP-15/T/10/20 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Double Elephant SX-302 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| Karina CLEAR PVC COMPOUND 80/268-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LIM3900-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |