Fortron® 0203
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ngyx5Y_Fortron-0203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A very easy flowing unfilled grade. This grade demonstrates excellent chemical resistance and thermal stability. Intended for extrusion applications that do not require high melt strength and for compounding with various fillers. Available as Fortron 0203B6 (granular powder), 0203P6 (pellets), and 0203C6 (crystallized pellets). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 | g/cm³ | ASTM D792 |
| -- | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 to 1.2 | % | |
| Across Flow | 0.80 to 1.0 | % | |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| M-Scale | 93 | ASTM D785 | |
| M-Scale | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Break, 23°C | 86.2 | MPa | ASTM D638 |
| Break | 33.0 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Break, 23°C | 3.0 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 3900 | MPa | ISO 178 |
| Flexural Stress 1 | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 95.0 | °C | ISO 75-2/C |
| Glass Transition Temperature 2 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 280 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 5.5E-5 | cm/cm/°C | |
| Transverse | 5.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 4 | 18 | kV/mm | ASTM D149 |
| -- | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 8.4E-3 | IEC 60250 | |
| Arc Resistance | 124 | sec | ASTM D495 |
| Comparative Tracking Index | 100 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity of Melt | 1830 | J/kg/°C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® 500450M | ELASTO | SEBS | Mediprene® |
| AcryliMax 301HP | S&E Specialty Polymers, LLC | ABS | AcryliMax |
| apirex® MBL 35 UV | API SpA | TPU-Polyether | apirex® |
| HIPEX® HX8ICN (Series: HTR/OR) | KRAIBURG TPE | TPE | HIPEX® |
| Lumiplas® LD7850 | LG Chem Ltd. | PC | Lumiplas® |