FRblend® PBT-1304
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NdfrWy_FRblend-PBT-1304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PBT-1304 is an unfilled, halogen-free flame retardant polybutylene-terephalate compound. The flame retardant system is base on non-chlorinated and non-brominated. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3870 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2860 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 90.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 9210-403 | Dongguan Top Polymer Enterprise | TPV | Topolymer® |
| ALTECH® PA66 B 1000/517 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Cri-Line FKHT-717 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| INELEC PPSCF40 | Infinity LTL Engineered Compounds | PPS | INELEC |
| LNP™ LUBRICOMP™ OFL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |