Zhongfa PA66 ST-24
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Yuyao Zhongfa Engineering Plastics Co. Ltd. |
| Trademark: | Zhongfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ncd4Fn_Zhongfa-PA66-ST-24.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zhongfa PA66 ST-24 is a polyamide 66 (nylon 66) material,. This product is available in the Asia-Pacific region and is processed by injection molding. The main characteristics of Zhongfa PA66 ST-24 are: impact resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 8.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 46.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 180 | % | ASTM D638 |
| Flexural Modulus | 1310 | MPa | ASTM D790 |
| Flexural Strength | 59.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 62.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 89.6 kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 6.0 - 8.0 | hr | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PET IV 76 WB | Marco Polo International, Inc. | PET | MARPOL® PET |
| Vydyne® 63A | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ALTECH® PA66 C 2030/116 GF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| LNP™ LUBRICOMP™ EL002 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| Latiohm 82-02 PD09 | LATI S.p.A. | Nylon 12 | Latiohm |