Hiflex CA 7600 A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hiflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NcVtg8_HiflexCA7600A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hiflex CA 7600 A is a reactor soft thermoplastic polyolefin (TPO) , manufactured using the LyondellBasell proprietary Catalloy process technology and is stabilized with a standard additive package. The grade is available in natural colored pellet form. Hiflex CA 7600 A is designed for use in injection molding or extrusion compounds when high processability, optimum mechanical and dimensional stability, are key properties. Thanks to its tailored elastomeric phase, Hiflex CA 7600 A features high softness and high toughness at very low temperature and provide high thermal characteristics. Hiflex CA 7600 A is used as a blending partner to improve the overall performances of esthetical interior and exterior automotive parts. Hiflex CA 7600 A provides high filler loading capability and is highly compatible with a wide range of polyolefins and soft plastics. This grade can be either blended or co-extruded with other materials to provide the required property balance. For regulatory information please refer to Hiflex CA 7600 A Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.880 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 26 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 11.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 600 | % | ISO 527-2 |
| Flexural Modulus | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 110 | kJ/m² | ISO 179/1eA |
| -20°C | No Break | ISO 179/1eA | |
| 23°C | No Break | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 45.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 58.0 | °C | ISO 306/A50 |
| Melting Temperature | 163 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torelina® A504X95 | Toray Resin Company | PPS | Torelina® |
| AKROMID® A3 GF 15 1 black (2382) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| BLUESTAR® PBT 101G0 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| CERTENE™ LLHF-0825F | Muehlstein | LLDPE | CERTENE™ |
| Ultramid® A3WG7 HR BK23591 | BASF Corporation | Nylon 66 | Ultramid® |