Order Products : sales@su-jiao.com
SABIC® HDPE M200056
| Category: | HDPE , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nc9Mwk_SABICHDPEM200056.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
M200056 is High Density Polyethylene grade with narrow molecular weight distribution suitable for injection molding applications. It has been designed to give good flow properties, low warpage with good dimensional stability and high gloss. Typical Applications M200056 is recommended for houseware, food containers, toys, caps and closures etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693B | ||
| 10% Igepal, molded, F50 | 2.00 | hr | ASTM D1693B |
| 100% Igepal, molded, F50 | 3.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (Injection Molded) | 800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, injection molding | 24.0 | MPa | ASTM D638 |
| Fracture, injection molding | 12.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Injection Molded) | > 200 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 825 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 23.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Injection Molded) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 250 | °C | |
| Middle Temperature | 180 - 250 | °C | |
| Front Temperature | 180 - 250 | °C | |
| Mold Temperature | 15.0 - 60.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 4000-50A | Vi-Chem Corporation | TPE | Sevrene® |
| Novalloy-A A2602 | Daicel Polymer Ltd. | ABS+Nylon | Novalloy-A |
| Durolon® HFR1900 | Unigel Plásticos | PC | Durolon® |
| ELASTOSIL® E 303 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| Koylene SM100N | Reliance Industries Limited | PP Homopolymer | Koylene |