Propafilm™ SRC95
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NbubdA_Propafilm-SRC95.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shrink Tightening Acrylic Coated Film Biaxially oriented polypropylene (BOPP) film coated on both sides with an aqueous acrylic (chlorine free) dispersion. SRC95/110 are suitable for use as a carton, naked collation or bundle overwrap in the tobacco or other packaging industries where exceptional appearance, aroma barrier and wrap tightness are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 80°C, 1 min | 1.5 | % | |
| Flow : 120°C, 1 min | 6.0 | % | |
| Across Flow : 80°C, 1 min | 1.0 | % | |
| Across Flow : 120°C, 1 min | 9.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.20 to 0.30 | ||
| vs. Itself - Static, Outside/Outside | 0.20 to 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 2400 | µm | |
| Seal Strength 1 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature 2 | 85.0 to 143 | °C | Internal Method |
| Oxygen Permeability | ASTM F1927 | ||
| 23°C, 85% RH | 19 | cm³·mm/m²/atm/24 hr | |
| 25°C, 0% RH | 22 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate | ASTM F1770 | ||
| 23°C, 85% RH | 0.93 | g/m²/24 hr | |
| 38°C, 90% RH | 5.4 | g/m²/24 hr | |
| Yield | 45.7 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 90 | ASTM D2457 | |
| Haze 3 | 2.0 to 2.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 266°F; 1sec; 15lb/in² |
| 2 . | 2secs; 15psi |
| 3 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Ferro PP TPP10AT17BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Fluon® PTFE PB1202 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Geon™ Vinyl Wire & Cable WR8180L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| LNP™ THERMOCOMP™ RF004XXD compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |