Daelim Po1y® XP9400
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NaqpL7_DaelimPo1yXP9400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®XP9400 is a metallocene linear low density polyethylene product,. It is available in Europe or Asia Pacific. Daelim Po1y®The application areas of XP9400 include wrapping, packaging, film and food contact applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.915 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 22 µm, extruded film | 44.1 | MPa | ASTM D882 |
| TD : Fracture, 22 µm, extruded film | 36.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 22 µm, extruded film | 470 | % | ASTM D882 |
| TD : Fracture, 22 µm, extruded film | 650 | % | ASTM D882 |
| Dart Drop Impact (22 µm, cast film) | 550 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| Peak Melting Temperature | 114 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45, 22.0 µm, cast film) | 100 | ASTM D2457 | |
| Haze (22.0 µm, cast film) | 0.30 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 30 T UV LE | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| Surlyn® 9320 | DuPont Packaging & Industrial Polymers | EMAA | Surlyn® |
| Moplen F39S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| AEI SX528 | AEI Compounds Limited | XLPE | AEI |
| EPLAMID 66 GFS 20 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |