CAPROWAX P™ 6006-11-000 Granulat
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | POLYFEA |
| Trademark: | CAPROWAX P™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NaPhK3_CAPROWAX-P-6006-11-000-Granulat.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The new biodegradable material system is particulary suited for the cycle of matter for use in agriculture, horticulture, landscaping, nursery, viniculture, greenhouse, floristic and forestry. Products made of CAPROWAX P™: Slow decomposition in soil, quick decomposition in compost into organic substances, carbon dioxide and water. Product surfaces are cleaning by them self with water or rain just like lotus flowers. CAPROWAX P™ is composed of polymers and waxes, which are permitted in partitions of food packaging. Further information on request. CAPROWAX P™- materials are processible like plastics and contain nevertheless by the majority parts of renewable materials. The processing without pre-drying under moderate temperatures, low shear rates and pressures is especially suited nature fabrics and heat-sensitve additives. The stability against water/mildewing and the balanced mixture of stable in use, composting and rotting is exemplary. The recipes of CAPROWAX P™- Compounds are granted by european patent office. They consist of mixtures from aliphatic polyester and modified herbal triglycerides |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 to 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (90°C/2.16 kg) | 2.50 to 10.0 | cm³/10min | ISO 1133 |
| Ash Content 1 | 2.4 to 2.6 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blow Molding Temperature | 80 to 150 | °C | |
| Softening Range | 57 to 63 | °C | DSC |
| Thermoforming Molding Temperature | 75 to 85 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Residual Moisture Content 2 | < 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 54 | ISO 868 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 56.0 | °C | ISO 306/A50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 48.0 to 50.0 | °C | |
| Melt Temperature | 100 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 500°/25 min |
| 2 . | 60 min/90°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2501TH00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Wellamid® GF33-66/6 XE-NBK1 | Wellman Engineering Resins | Nylon 66/6 | Wellamid® |
| DuraFlex 826 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| OPTODYNE™ UV-3100 | DAIKIN AMERICA, INC. | Epoxy | OPTODYNE™ |
| NORYL GTX™ GTX902D resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |