Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ AF001H compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NZsse9_LNP-THERMOCOMP-AF001H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AF001H is a compound based on ABS resin containing 5% Glass Fiber. Added feature of this material is: Healthcare. Also known as: LNP* THERMOCOMP* Compound AF-1001 HC Product reorder name: AF001H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2750 | MPa | ASTM D638 |
| Tensile Strength (Break) | 40.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 2740 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8948-50 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nypol® PA B3 G10 PRTA011 NT390 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| DJSilicone NE-9440 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Extir® CM Giotto 5 | Versalis S.p.A. | PS (EPS) | Extir® |
| HANWHA CP-710 | Hanwha Chemical | PVC Copolymer | HANWHA |