STYRON A-TECH™ 1173
| Category: | PS (HIPS) , Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON A-TECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NZr4d9_STYRON-A-TECH-1173.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON A-TECH™ 1173 advanced technology polystyrene resin is a high impact, environmental stress crack resistant (ESCR) resin for extrusion thermoforming applications. The improved rigidity of this resin allows potential down-gauging and scrap reduction, as well as overall improvements in process efficiency. Main Characteristics:
Complies with:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 13.1 | MPa | |
| Yield, Injection Molded | 17.2 | MPa | |
| Break, Compression Molded | 15.9 | MPa | |
| Break, Injection Molded | 27.6 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, Compression Molded | 30 | % | |
| Break, Injection Molded | 55 | % | |
| Flexural Modulus | ASTM D790 | ||
| Compression Molded | 1200 | MPa | |
| Injection Molded | 1510 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Compression Molded | 27.6 | MPa | |
| Injection Molded | 40.7 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, Compression Molded | 80 | J/m | |
| 23°C, Injection Molded | 90 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 71.1 | °C | |
| 1.8 MPa, Annealed | 97.8 | °C | |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3897 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| POLYPRO® 5010 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Xuchuan XCY-5036 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Anjacom® 350-H/GF30 | Almaak International GmbH | Nylon 66 | Anjacom® |
| Romiloy® 9170E | ROMIRA GmbH | PC+ABS | Romiloy® |