Radel® R-7625 Datasheet,PPSU,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Radel® R-7625 polyphenylsulfone resin is a cost-effective solution for aircraft interior applications that offers improved UV resistance versus Radel® R-7535 and Radel® R-7558. The product complies with the FAA regulation 14CFR Part 25 Appendix F, offering vertical burn resistance, very low smoke generation and, through the use of proprietary additives, low heat release values, when tested using the Ohio State University (OSU) rate of heat release method. It also generates low flaming-mode toxic gas emissions. Radel® R-7625 resin is available in light colors and is formulated for integrally colored applications. Available in several custom colors

General Information
Features	Low smoke Low toxicity Good processing stability Good liquidity Detergent resistance Good toughness Flame retardancy
Uses	Airplane trim Aircraft applications Aerospace applications
Agency Ratings	FAA FAR 25.853a FAA FAR 25.853d
RoHS Compliance	Contact manufacturer
Appearance	Available colors
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity ¹	1.36	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (380°C/2.16 kg)	17	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.60 - 0.80	%	ASTM D955
Water Absorption (24 hr)	0.30	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2830	MPa	ASTM D638
Tensile Strength	86.2	MPa	ASTM D638
Tensile Elongation (Break)	30	%	ASTM D638
Flexural Modulus	2760	MPa	ASTM D790
Flexural Strength	121	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	69	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	193	°C	ASTM D648

Flammability	Nominal Value	Unit	Test Method
OSU peak heat release rate ²		kW/m²	FAR 25, AppF
OSU total heat release- 2 minutes ³		kW·min/m²	FAR 25, AppF
Vertical combustion -60 seconds ⁴			FAR 25, AppF
Dripping burning time	No drip	sec	FAR 25, AppF
Burning time	0.0	hr	FAR 25, AppF
Length		cm	FAR 25, AppF
Smoke density- Smoke density at 4 minutes ⁵			FAR 25, AppF

Injection	Nominal Value	Unit
Drying Temperature	166 - 177	°C
Drying Time	4.0	hr
Rear Temperature	354 - 371	°C
Middle Temperature	360 - 377	°C
Front Temperature	366 - 382	°C
Nozzle Temperature	360 - 377	°C
Processing (Melt) Temp	366 - 388	°C
Mold Temperature	107 - 163	°C
Injection Rate	Fast
Screw Compression Ratio	2.0 : 1.0 - 3.0 : 1.0

Injection instructions
Drying: Radel R-7625 resin must be thoroughly dried prior to melt processing. Incomplete drying will result in defects in molded parts ranging from surface streaks to severe bubbling. Pellets can be dried using shallow trays placed in a circulating air oven or in a desiccating hopper dryer. Recommended minimum drying conditions are 4 hours at 149°C (300°F). Drying at 165°C to 177°C (330°F to 350°F) is preferable. Injection Molding: Radel R-7625 resin can be readily injection molded in most screw injection machines. A general purpose screw with a 2 to 3:1 compression ratio is recommended, as is minimum back pressure. Injection speeds should be as fast as possible, consistent with part appearance requirements. Mold temperatures in the range of 107°C to 163°C (225°F to 325°F) are suggested. Melt temperature should generally range from 336°C to 388°C (690°F to 730°F). Caution: Exceeding 415°C (780°F) during processing may cause degradation.

Injection instructions

Drying: Radel R-7625 resin must be thoroughly dried prior to melt processing. Incomplete drying will result in defects in molded parts ranging from surface streaks to severe bubbling. Pellets can be dried using shallow trays placed in a circulating air oven or in a desiccating hopper dryer. Recommended minimum drying conditions are 4 hours at 149°C (300°F). Drying at 165°C to 177°C (330°F to 350°F) is preferable. Injection Molding: Radel R-7625 resin can be readily injection molded in most screw injection machines. A general purpose screw with a 2 to 3:1 compression ratio is recommended, as is minimum back pressure. Injection speeds should be as fast as possible, consistent with part appearance requirements. Mold temperatures in the range of 107°C to 163°C (225°F to 325°F) are suggested. Melt temperature should generally range from 336°C to 388°C (690°F to 730°F). Caution: Exceeding 415°C (780°F) during processing may cause degradation.

Note Message
1 .	Change by resin color
2 .	The purpose of the flammability test results is not to reflect the danger of these or any other materials under actual fire conditions.
3 .	The purpose of the flammability test results is not to reflect the danger of these or any other materials under actual fire conditions.
4 .	The purpose of the flammability test results is not to reflect the danger of these or any other materials under actual fire conditions.
5 .	The purpose of the flammability test results is not to reflect the danger of these or any other materials under actual fire conditions.

Category:	PPSU , Polyphenylsulfone
Manufacturer:	Solvay Specialty Polymers
Trademark:	Radel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NZmHrv_Radel-R-7625.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 300 HF FR A	RTP Company	PC	RTP
Vibrathane® B821	Chemtura	PUR-Ether/MDI	Vibrathane®
Andur 1-83 AP/Curene® 442	Anderson Development Company	PUR-Ether/TDI	Andur
Sylvin 8600-85 Brown 7417	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Sylvin 8353-80FUV White 1513	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin