Generic ABS+Nylon
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NZP7k9_Generic-ABS-Nylon.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+Nylon This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 - 1.09 | g/cm³ | ASTM D792 |
| 23°C | 1.05 - 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.28 - 0.73 | % | ASTM D955 |
| 23°C | 0.79 - 1.1 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.49 - 1.1 | % | ASTM D570 |
| 23°C, 24 hr | 0.50 - 0.71 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.1 - 1.4 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 101 - 102 | ASTM D785 | |
| 23°C | 115 - 117 | ISO 2039-2 | |
| Ball Indentation Hardness | 70.0 - 86.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 900 - 2300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 30.4 - 47.3 | MPa | ASTM D638 |
| Yield, 23°C | 27.0 - 95.8 | MPa | ISO 527-2 |
| Fracture, 23°C | 31.0 - 117 | MPa | ASTM D638 |
| 23°C | 34.8 - 45.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 3.0 - 3.9 | % | ISO 527-2 |
| Fracture, 23°C | 2.5 - 200 | % | ASTM D638 |
| Fracture, 23°C | 26 - 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 814 - 7170 | MPa | ASTM D790 |
| 23°C | 1150 - 2310 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 39.3 - 150 | MPa | ASTM D790 |
| 23°C | 41.4 - 74.3 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.7 - 82 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 99 - 820 | J/m | ASTM D256 |
| 23°C | 64 - 71 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 77.5 - 220 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 69.2 - 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.1 - 200 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 59.1 - 80.4 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 90.0 - 199 | °C | ASTM D1525 |
| -- | 99.9 - 191 | °C | ISO 306 |
| CLTE - Flow | 4.8E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 9.8E+13 - 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 - 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 650 - 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 95.9 | °C | |
| Drying Time | 2.9 - 5.0 | hr | |
| Rear Temperature | 195 - 260 | °C | |
| Middle Temperature | 234 - 268 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Nozzle Temperature | 235 - 241 | °C | |
| Processing (Melt) Temp | 230 - 265 | °C | |
| Mold Temperature | 59.3 - 80.0 | °C | |
| Back Pressure | 0.300 - 15.0 | MPa | |
| Screw Speed | 44 - 75 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+NylonThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP D130C | Braskem America Inc. | PP Homopolymer | Braskem PP |
| Fiberfil® J-60/15/UV/HS | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Gallonprene® GP520-8501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Plexiglas® Resist zk6HF | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| ISOTHANE® 8309 | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU, Unspecified | ISOTHANE® |