InnoTooling™ IE-9060
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTooling™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NYGNG2_InnoTooling-IE-9060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-9060 is a slow reacting polyurethane formulated for room temperature hand mix dispensing methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. This product is especially developed for translucent mass castings. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.06 | g/cm³ | |
| Cured | 1.07 | g/cm³ | |
| Matrix resin | 1.10 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 24.8 | MPa | ASTM D790 |
| Flexural Strength | 13.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 750 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by capacity: 100 Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by capacity: 42 Mixing ratio by weight: 40 | ||
| Demold Time | 180 - 420 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.15 | Pa·s | |
| 25°C 2 | 3.3 | Pa·s | |
| 25°C 3 | 6.9 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 14 - 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 50 - 60 | ASTM D2240 | |
| Tensile Strength | 22.4 | MPa | ASTM D638 |
| Tensile Elongation at Break | 250 | % | ASTM D638 |
| Tear Strength | 96.3 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safrene® C 7260 | Safripol (PTY) LTD | HDPE | Safrene® |
| Unilex™ UP 0100 | United Polychem | LDPE | Unilex™ |
| Axiall PVC 19855 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hostacom CR 250 F M G31463 | LyondellBasell Industries | PP Copolymer | Hostacom |
| ESTOPLAST XU 245NN01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |