NILFLEX® 10 K15TE
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NXlrVf_NILFLEX-10-K15TE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer high flow 15% mineral filled, high impact, good surface appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 - 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.0 - 1.4 | % | Internal method |
| Flow direction | 1.0 - 1.4 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 75 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 200 | J/m | ASTM D256 |
| Unnotched Izod Impact (0°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(600°C) | 15 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafoil™ RVG120 | Innovia Films Ltd. | PP Alloy | Propafoil™ |
| TRISTAR® PC-08 | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Xuchuan XCS-100P | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Cellophane™ 600P23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Hifax TRC 228P 2 C12637 | LyondellBasell Industries | PP Copolymer | Hifax |