DOWLEX™ 2645.01G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NX5g9f_DOWLEX-2645-01G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX 2645.01G™ Polyethylene Resin is designed for the production of a wide variety of industrial and consumer films (though it is not reccomended for silage stretch film). Films made from this resin exhibit a combination of excellent toughness and tear resistance. The product also delivers very good processability on conventional LLDPE machinery. DOWLEX 2645.01G Polyethylene Resin contains slip and antiblock additives. Applications:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Energy (50 µm) | 5.80 | J | ASTM D5748 |
| Film Puncture Force (50 µm) | 76.0 | N | ASTM D5748 |
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD : 50 µm | 139 | MPa | ISO 527-3 |
| 2% secant, TD : 50 µm | 147 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 7.50 | MPa | ISO 527-3 |
| TD : Yield, 50 µm | 6.30 | MPa | ISO 527-3 |
| MD : Break, 50 µm | 39.0 | MPa | ISO 527-3 |
| TD : Break, 50 µm | 40.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 560 | % | ISO 527-3 |
| TD : Break, 50 µm | 670 | % | ISO 527-3 |
| Dart Drop Impact (50 µm) | 480 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 50 µm | 560 | g | ASTM D1922 |
| TD : 50 µm | 910 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 43 | ASTM D2457 | |
| Haze (50.0 µm) | 18 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 模具间隙：1.5 - 2.5 mm 熔体温度：190 至 240°C 放大比：1.5 比 3.1 |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP110-13-45 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Nylfor® A2 GF/30 E2/2A NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Dryflex® A2 660701 | ELASTO | SEBS | Dryflex® |
| LUBAN™ 1101 S | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |
| Rotuba CA MS | Rotuba Extruders, Inc. | CA | Rotuba CA |