| Arlon 44N is a high resin content multifunctional (175°C) epoxy prepreg system with a proprietary micordisperse ceramic filler system. 44N is engineered for the filling of clearance holes in thin Metal cores such as 0.006" Copperinvar- Copper or via holes in sequentially laminated MLB designs. Based on Arlon's 45N, the 44N system is compatible with conventional epoxy lamination and fabrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.85 | g/cm³ | ASTM D792A |
| Water Absorption (24 hr) | 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19300 | MPa | Internal Method |
| Poisson's Ratio 1 | 0.15 | ASTM D3039 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | Internal Method | ||
| -- 2 | 1.4 | kN/m | |
| -- 3 | 1.4 | kN/m | |
| -- 4 | 1.4 | kN/m |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 5 | 2.4 | % | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 175 | °C | Internal Method |
| CLTE - Flow | |||
| -- 6 | 1.4E-5 to 1.6E-5 | cm/cm/°C | Internal Method |
| < 175°C 7 | 5.5E-5 | cm/cm/°C | Internal Method |
| > 175°C 8 | 2.0E-4 | cm/cm/°C | Internal Method |
| Thermal Conductivity (100°C) | 0.30 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | Internal Method | ||
| -- 9 | 2.9E+13 | ohms | |
| -- 10 | 4.0E+10 | ohms | |
| Volume Resistivity | Internal Method | ||
| -- 11 | 2.6E+13 | ohms·cm | |
| -- 12 | 3.3E+13 | ohms·cm | |
| Dielectric Strength | 59 | kV/mm | Internal Method |
| Dielectric Constant 13(1 MHz) | 4.40 | Internal Method | |
| Dissipation Factor (1 MHz) | 0.025 | Internal Method | |
| Arc Resistance | 65.0 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | x and y direction |
| 2 . | After Thermal Stress |
| 3 . | After Process Solutions |
| 4 . | At Elevated Temperatures |
| 5 . | Z-axis |
| 6 . | X-axis |
| 7 . | Z-axis |
| 8 . | Z-axis |
| 9 . | E24/125 |
| 10 . | C96/35/90 |
| 11 . | E24/125 |
| 12 . | C96/35/90 |
| 13 . | Range: 402 to 406 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra HoPP 35 | ResMart | PP Homopolymer | ResMart Ultra |
| EvoSource™ ABS 4535 90/05 | MBA Polymers | ABS | EvoSource™ |
| Formolene® E927 | Formosa Plastics Corporation, U.S.A. | HDPE, HMW | Formolene® |
| DynaChar™ 5565-C | Polymer Dynamix | TPE | DynaChar™ |
| SQUARE® LIM1962-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |