Extrusion/Thermoforming Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Break | 3.00 | MPa | ISO 527-2/1A/5 |
| Break | 110 | MPa | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 11700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | °C | ISO 75-2/A |
| Melting Temperature 1 | 357 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® ABS FC 1000/106 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |
| Celstran® PP-GF20-0553 Black | Celanese Corporation | PP Copolymer | Celstran® |
| EMOPLEN® A 830 G3 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| ENFLEX S3340A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Hostacom D M2 T32 | LyondellBasell Industries | PP Copolymer | Hostacom |