| TECHNYL® C 218 V30 Black is a polyamide 6, heat stabilized, reinforced with 30% of glass fiber, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.430 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9600 | 6200 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Break | 170 | -- | MPa | ASTM D638 |
| Break | 190 | 110 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 3.5 | -- | % | ASTM D638 |
| Break | 3.2 | 4.5 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 8900 | -- | MPa | ASTM D790 |
| -- | 8400 | 4900 | MPa | ISO 178 |
| Flexural Strength | 255 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 32 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 92 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 130 | -- | J/m | ASTM D256 |
| 23°C | 14 | 24 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 3.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.80 | 4.50 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 475 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.400 to 3.20 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 to 3.20 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 245 to 250 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reblend® 5510M4 NERO | SO.F.TER. SPA | PC+ABS | Reblend® |
| Sylvin 9737-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CELLOMER® 2100 | Microcell Composite Company | SBS | CELLOMER® |
| POLYfill PPHC GF3030 PD2 | Polykemi AB | PP, Unspecified | POLYfill |
| TECHNYL® B 216 BLACK 3N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |