Eltex® P KV409

Category:	PP Random Copolymer , Polypropylene Random Copolymer
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex® P
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NRYgiH_Eltex-P-KV409.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Polypropylene - Heat Seal Benefits & Features Eltex® P KV409 is a random copolymer with a high ethylene content, developed for use primarily as the sealing layer in "co-extruded bi-oriented film". It contains no special additives and is thus particularly appreciated by users wishing to use their own "formulas". Superior optical properties than Eltex ® P KS409 (lower haze, higher clarity) Applications Random copolymer specially developed for the sealing layers of "co-extruded bi-oriented film", suitable also for co-extruded cast film.

Message

Polypropylene - Heat Seal

Benefits & Features
Eltex® P KV409 is a random copolymer with a high ethylene content, developed for use primarily as the sealing layer in "co-extruded bi-oriented film". It contains no special additives and is thus particularly appreciated by users wishing to use their own "formulas".

Superior optical properties than Eltex ® P KS409 (lower haze, higher clarity)

Applications

Random copolymer specially developed for the sealing layers of "co-extruded bi-oriented film", suitable also for co-extruded cast film.

General Information
Features	Additive Free Opticals Random Copolymer
Uses	Bi-axially Oriented Film Cast Film
RoHS Compliance	Contact Manufacturer
Forms	Pellets
Processing Method	Coextruded Film

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.895	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	7.0	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus (23°C)	750	MPa	ISO 178

Films	Nominal Value	Unit	Test Method
Heat Seal Threshold ¹	115	°C	Internal Method

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	60.0	°C	ISO 75-2/B
Vicat Softening Temperature	120	°C	ISO 306/A50
Melting Temperature	134	°C	ASTM D3417

Note Message
1 .	1s, 3 bars, 100 mm/min, 100 g/cm

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC 6917 WT020	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
Megalon® 113GL	Mega Polymers	Nylon 66	Megalon®
Karina RED PVC COMPOUND 902-42/291-IS (*)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Petrothene® NA336	LyondellBasell Industries	LDPE	Petrothene®
Crastin® LW9320LM BK591	DuPont Performance Polymers	PBT	Crastin®