Order Products : sales@su-jiao.com
Iupilon® MB2112N
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NPZZq2_Iupilon-MB2112N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® MB2112N is a Polycarbonate + Polyester (PC+Polyester) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® MB2112N are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.60 to 0.80 | % | |
| Flow : 3.20 mm | 0.60 to 0.80 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.9 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 93 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 71 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 138 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 116 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 6.1E-5 | cm/cm/°C | |
| Transverse | 7.1E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ren Ren Shape 550 | Huntsman Advanced Materials | PUR, Unspecified | Ren |
| TEREZ PA/PP 7500 GF 7/1 | TER HELL PLASTIC GMBH | Nylon 6+PP | TEREZ PA/PP |
| ELASTOSIL® R plus 4020/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Grilamid® XE 4071 nat | EMS-GRIVORY | Nylon 612 | Grilamid® |
| PLUSTEK PD300G5 | Polyram Ram-On Industries | Nylon 12 | PLUSTEK |