SABIC® HDPE M40060S
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NP6U5M_SABIC-HDPE-M40060S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE M40060S is an UV stabilized, high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It has improved mouldability. Articles produced from this grade typically show good impact strength, low warpage, stress crack resistance (ESCR) and good gloss. Typical applications. SABIC® HDPE M40060S is typically used for the manufacture of injection moulded articles such as pails, shipping containers and industrial parts. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.0 | g/10 min | |
| 190°C/5.0 kg | 11 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 70.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1300 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 30.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 24.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1500 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 5.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature (DSC) | 133 | °C | ISO 11357-3 |
| Enthalpy Change | 219 | J/g | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Pressure | 93.0 to 103 | MPa |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V916 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tecomid® NA40 NL E | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Sicostirolo 684V0 | Ravago Group | PS (HIPS) | Sicostirolo |
| Terraloy™ MB-10000A | Teknor Apex Company | TPS+LLDPE | Terraloy™ |
| LNP™ LUBRICOMP™ DFL32XXP compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |