DESTRON™ DSC1701GH5
| Category: | PPA , Polyphthalamide |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESTRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NOzSLc_DESTRON-DSC1701GH5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESTRON™ DSC1701GH5 is semi-crystalline PPA(Polyphthalamide) Glass fiber 25% reinforced grade. It has great mechanical properties, good dimensional stability and excellent thermal performance. Applications: DESTRON™ DSC1701GH5 is applicable for automotive industry, electrical items and several industrial equipment like water outlet. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 - 0.90 | % | |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 167 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.2 | % | ASTM D638 |
| Flexural Modulus | 7650 | MPa | ASTM D790 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 280 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 240 | °C | ASTM D648 |
| Melting Temperature | 310 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 135 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 310 - 320 | °C | |
| Middle Temperature | 315 - 345 | °C | |
| Front Temperature | 320 - 345 | °C | |
| Nozzle Temperature | 320 - 345 | °C | |
| Processing (Melt) Temp | 320 - 345 | °C | |
| Mold Temperature | 100 - 140 | °C |
| Injection instructions |
|---|
| Speed: 40 to 70%Pressure 1st: 30 to 60%Pressure 2nd: 30 to 60Holding Pressure: 10 to 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPLEN 0024 V2 LBC | Vamp Tech | PP Homopolymer | VAMPLEN |
| Alathon® M6138 | LyondellBasell Industries | HDPE | Alathon® |
| AKROMID® A3 GK 30 1 natural (3673) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| PIVINEL™ NEX-LTH1-LF | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| LEXAN™ 955 resin | SABIC Innovative Plastics | PC | LEXAN™ |