Zytel® HTN 92G45DH2 BK083
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NMNkxq_Zytel-HTN-92G45DH2-BK083.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, PPA, High Performance Polyamide with DuPont |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.54 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 15000 | 12500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 214 | 168 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 13000 | -- | MPa | ISO 178 |
| Flexural Stress | 300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 11 | -- | kJ/m² | |
| 23°C | 11 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | -- | kJ/m² | |
| 23°C | 70 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 284 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 310 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | 31 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic PVDF 315080003 | 3M Advanced Materials Division | PVDF | 3M™ Dyneon™ Fluoroplastic |
| Nypol® PA A3 G30 PRTA011 NR398 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| NYLEM® 66 GTF 45 | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| KRATON® D1161 B | Kraton Polymers LLC | SIS | KRATON® |
| Sylvin 4215-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |