Aegis® H135ZP Datasheet,Nylon 6,Honeywell-SHANGHAI SUSHENG

Message
Aegis® H135ZP is a high viscosity nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermoforming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.

General Information
Features	Homopolymer Good strength Good wear resistance Good chemical resistance Heat resistance, high Good toughness Viscosity, High
Uses	Packaging cast film
Agency Ratings	FDA 21 CFR 177.1500 European 2002/72/EC
Forms	Particle
Processing Method	Film extrusion Blow film cast film Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.13	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (235°C/1.0 kg)	1.2	g/10 min	ASTM D1238
Water Absorption			ASTM D570
24 hr	1.6	%	ASTM D570
Saturation	9.5	%	ASTM D570
Balance	2.7	%	ASTM D570
Moisture Content		%	ASTM D6869
Relative viscosity- @ 96% Sulfuric Acid	3.75
Viscosity- FAV	135		ASTM D789

Films	Nominal Value	Unit	Test Method
Elmendorf Tear Strength			ASTM D1922
MD : 23°C	860	N	ASTM D1922
TD : 23°C	990	N	ASTM D1922
Graves Tear			ASTM D1004
MD : 23°C	2170	N	ASTM D1004
TD : 23°C	2380	N	ASTM D1004

Additional Information	Nominal Value	Unit
Puncture Index (23°C) ¹	470.000	g/cm³
Puncture Resistance (23°C) ²	1100	g

Films	Nominal Value	Unit	Test Method
Elastic Modulus - MD ³	660	MPa	ASTM D882
Elastic Modulus - TD ⁴	640	MPa	ASTM D882
Tensile Strength ⁵			ASTM D882
MD : Yield	30.0	MPa	ASTM D882
TD : Yield	30.0	MPa	ASTM D882
MD : Fracture	90.0	MPa	ASTM D882
TD : Fracture	90.0	MPa	ASTM D882
Tensile Elongation ⁶			ASTM D882
MD : Fracture	330	%	ASTM D882
TD : Fracture	330	%	ASTM D882
Carbon Dioxide Transmission Rate (23°C)	72.8	cm³/m²/24 hr	ASTM D1434
Nitrogen Transmission Rate (23°C)	14.0	cm³/m²/24 hr	ASTM D1434
Oxygen Transmission Rate (23°C)	40	cm³/m²/24 hr	ASTM D3985
Water Vapor Transmission Rate (38°C, 100% RH)	990	g/m²/24 hr	ASTM F1249

Thermal	Nominal Value	Unit
Melting Temperature	220	°C

Additional Information	Nominal Value	Unit
Extractible Content: 0.7 %

Extrusion	Nominal Value	Unit
Drying Temperature	80.0	°C
Cylinder Zone 1 Temp.	230 - 260	°C
Cylinder Zone 2 Temp.	230 - 260	°C
Cylinder Zone 3 Temp.	230 - 260	°C
Cylinder Zone 4 Temp.	230 - 260	°C
Cylinder Zone 5 Temp.	230 - 260	°C
Adapter Temperature	260 - 266	°C
Melt Temperature	260 - 270	°C
Die Temperature	260	°C

Extrusion instructions
The values listed above in Extrusion are for cast film.Typical Barrel Profile for Tubular (Blown) Films: Barrel Temperature: 246 to 254°C (474 to 490°F) Adapter Temperature: 260°C (500°F) Die Temperature: 254°C (490°F) Processing Melt Temperature: 254 to 260°C (490 to 500°F) Screw Parameters: Metering section: 40% Transition section: 3 to 4 flights Feed section balance of screw length Compression ratio: 3.5:1 to 4.0:1 L/D ratio: 24:1

Extrusion instructions

The values listed above in Extrusion are for cast film.Typical Barrel Profile for Tubular (Blown) Films: Barrel Temperature: 246 to 254°C (474 to 490°F) Adapter Temperature: 260°C (500°F) Die Temperature: 254°C (490°F) Processing Melt Temperature: 254 to 260°C (490 to 500°F) Screw Parameters: Metering section: 40% Transition section: 3 to 4 flights Feed section balance of screw length Compression ratio: 3.5:1 to 4.0:1 L/D ratio: 24:1

Note Message
1 .	ASTM D1306
2 .	ASTM D1306
3 .	23°C
4 .	23°C
5 .	23°C
6 .	23°C

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	Aegis®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NM79ST_Aegis-H135ZP.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TABOND 3034	SILON s.ro	LDPE+LLDPE	TABOND
Verolloy A1300	PlastxWorld Inc.	ABS+Nylon	Verolloy
ACCUTECH™ CP0436C30L1	ACLO Compounders Inc.	PP Copolymer	ACCUTECH™
Amodel® AE-1133	Solvay Specialty Polymers	PPA	Amodel®
EMPILON® 680	EMPILON	SEBS	EMPILON®