Andur 8-5 APLS/Curene® 49
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NK1Ibb_Andur-8-5-APLS-Curene-49.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 8-5APLS is a polyester based, toluene diisocyanate terminated prepolymer designed for optimum solvent resistance. Elastomers with a Shore A durometer hardness of 83-86 can be obtained when Andur 8-5APLS is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of 53-56 Shore A durometer hardness can be obtained when cured with Curene 49. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 1.59 | MPa | ASTM D412 |
| 300% strain | 3.24 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 27.6 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 530 | % | ASTM D412 |
| Compression Set | 1.0 | % | ASTM D395B |
| Bayshore Resilience | 34 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 2.0 - 4.0 | min | |
| Demold Time | 30 | min | |
| Post Cure Time | |||
| 22°C | 72 | hr | |
| 99°C | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 53 to 56Die C Tear, ASTM D1004: 185 pliAverage Split Tear, ASTM D1938: 18 pliStoichiometry Curative Level: 105%Grams Curene 49 per 100 grams Andur 8 to 5 APLS: 4.4Mix Temperature: Andur 8-5 APLS: 180-220°F Curene 49: 110-120°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 98.9 - 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REPROCESSED PA6 8267-300R | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REPROCESSED |
| Beamset 255 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
| Etinox® 650 | Ercros, S.A. | PVC Homopolymer | Etinox® |
| Fire PRF2 1000 FM | Indspec Chemical Corporation | PF | Fire PRF2 |
| Plexiglas® Satinice df20 8N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |