Braskem PP CP 286
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NHWerd_Braskem-PP-CP-286.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CP 286 is a high melt flow rate, heterophasic copolymer, suitable for injection moulding applications and also as base resin for compound. The resin combines excellent stiffness with good impact resistance, even at sub-zero temperatures. Applications: Base resin for compounding, high impact resistance parts Processing: Injection Moulding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.895 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 22.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strain | |||
| Yield, Injection Molded | 6.0 | % | ISO 527-2 |
| Break, Injection Molded | 6.0 | % | ASTM D638 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1100 | MPa | ASTM D790 |
| Injection Molded | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 75 | J/m | ASTM D256 |
| 23°C, Injection Molded | No Break | ASTM D256 | |
| -20°C, Injection Molded | 8.5 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 47 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, Injection Molded | 103 | °C | |
| 1.8 MPa, Unannealed, Injection Molded | 54.0 | °C | |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DENISTAT P 00U 03 M | Vamp Tech | PP Copolymer | DENISTAT |
| Fainplast PVC MPH 73/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| HAIPLEN H30 G6 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Jampilen EP540N | Jam Polypropylene Company | PP Copolymer | Jampilen |
| TechnoDur PBT4 GF 30 Natural (9987) | TechnoCompound GmbH | PBT | TechnoDur |