CYROLITE® G-20 HIFLO®

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	CYROLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NEZrX5_CYROLITE-G-20-HIFLO-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

CYROLITE G-20 HIFLO compound is an impactmodified acrylic-based multipolymer for molding and extrusion of medical applications.

Typical properties of CYROLITE® acrylic-based multipolymer compounds are:

excellent chemical resistance to fats and oils

excellent bonding and welding capabilities

excellent bonding to PVC tubing

good impact strength

good light transmission

good resistance to EtO, gamma and E-beam sterilization

The special properties of CYROLITE G-20 HIFLO compound are:

excellent melt flow rate

good heat resistance

Used for injection molding and extrusion of medical devices, medical packaging, as well as toys and appliance parts.

General Information
Additive	Impact Modifier
Features	Bondability E-beam Sterilizable Ethylene Oxide Sterilizable Good Chemical Resistance Good Impact Resistance High Clarity High Flow Impact Modified Medium Heat Resistance Radiation Sterilizable Weldable
Uses	Appliance Components Bottles Connectors Medical Packaging Medical/Healthcare Applications Toys Valves/Valve Parts
Agency Ratings	EC 1907/2006 (REACH) FDA 21 CFR 177.1010 USP Class VI
Appearance	Clear/Transparent Colors Available
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.11	g/cm³	ASTM D792
Apparent Density	0.65	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/5.0 kg)	10	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.70	%	ASTM D955
Water Absorption (24 hr)	0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	27		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2550	MPa	ASTM D638
Tensile Strength (Yield)	48.3	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	3.6	%
Break	9.5	%
Flexural Modulus	2140	MPa	ASTM D790
Flexural Strength (Yield)	64.8	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 6.35 mm	59	J/m
23°C, 6.35 mm	100	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	85.6	°C	ASTM D648
Vicat Softening Temperature	101	°C	ASTM D1525
CLTE - Flow (0 to 156°C)	9.3E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	89.0	%	ASTM D1003
Haze (3200 µm)	6.0	%	ASTM D1003
Yellowness Index (3.20 mm)	-0.30	YI	Internal Method

Injection	Nominal Value	Unit
Drying Temperature	79.4	°C
Drying Time	3.0 to 4.0	hr
Processing (Melt) Temp	193 to 238	°C
Mold Temperature	48.9 to 82.2	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 1307 TFE 15	RTP Company	PPS	RTP
Baoding 67I98	Baoding Bangtai Polymeric New-Materials Co.,Ltd	TPU-Polyester	Baoding
Chemlon® 100 L	Teknor Apex Company (Chem Polymer)	Nylon 66	Chemlon®
Sylvin 8344-75 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LNP™ LUBRILOY™ RX99650 compound	SABIC Innovative Plastics	Nylon 66	LNP™ LUBRILOY™