LNP™ VERTON™ MV006S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NE7Sbn_LNP-VERTON-MV006S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON MV006S is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Structural. Also known as: LNP* VERTON* Compound MFX-7006 HS Product reorder name: MV006S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.59 | % | ISO 294-4 |
| Flow : 24 hr | 0.27 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7810 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 103 | MPa | ASTM D638 |
| Break | 105 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 6030 | MPa | ASTM D790 |
| -- | 6450 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 150 | MPa | ASTM D790 |
| -- | 153 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.36 | ||
| vs. Itself - Static | 0.39 | ||
| Wear Factor - Washer | 44.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 1 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 770 | J/m | ASTM D4812 |
| 23°C 2 | 50 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.0 | J | ASTM D3763 |
| -- | 10.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 158 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 221 to 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® PPA CF30 TS0 | EPIC Polymers | PPA | TRIBOCOMP® |
| Ultramid® B27 E | BASF Corporation | Nylon 6 | Ultramid® |
| Hanwha Total PP TB52L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| POTICON VCF442 | Otsuka Chemical Co., Ltd. | LCP | POTICON |
| REV Materials 8007 | REV Materials | Polyolefin, Unspecified | REV Materials |