Stanyl® TS200F10
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NDGF0T_Stanyl-TS200F10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stanyl® TS200F10 is a Polyamide 46 (Nylon 46) material filled with 50% glass fiber. It is available in Asia Pacific. Primary attribute of Stanyl® TS200F10: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.62 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 16000 | 10000 | MPa | |
| 120°C | 8200 | -- | MPa | |
| 160°C | 7400 | -- | MPa | |
| 180°C | 7000 | -- | MPa | |
| 200°C | 6600 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 250 | 160 | MPa | |
| Break, 120°C | 140 | -- | MPa | |
| Break, 160°C | 120 | -- | MPa | |
| Break, 180°C | 110 | -- | MPa | |
| Break, 200°C | 100 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 2.7 | 5.0 | % | |
| Break, 120°C | 5.0 | -- | % | |
| Break, 160°C | 5.0 | -- | % | |
| Break, 180°C | 5.0 | -- | % | |
| Break, 200°C | 5.0 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 14000 | 9000 | MPa | |
| 120°C | 7300 | -- | MPa | |
| 160°C | 6500 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 14 | kJ/m² | |
| 23°C | 16 | 24 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 100 | kJ/m² | |
| 23°C | 100 | 110 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 14 | 14 | kJ/m² | |
| 23°C | 16 | 24 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 300 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LC 185 A | A. Schulman Europe | ABS | POLYMAN® |
| NEFTEKHIM PS 430M | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| Ablefilm 561K | Henkel Ablestik | Epoxy | Ablefilm |
| G-Lex F55HM0003 | Gas Authority of India Limited | HDPE, HMW | G-Lex |
| Lucky PVC Recycle 50 | Lucky Plastics Industries (Pvt) Ltd. | PVC, Rigid | Lucky PVC |