TABOREX TA 1133 HD
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SILON s.ro |
| Trademark: | TABOREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NCNyiU_TABOREX-TA-1133-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A chemically-crosslinkable HDPE compound for the production of single and multi-layer pipes for domestic hot and cold water, under floor heating and central heating application. TABOREX TA 1132 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes which are produced with the SILON grade TABOREX TA 1132 HD fulfil the requirements of ASTM F876-04a, CSA 137.5-03, EN ISO 15875, BS 7291 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer and will attain a high level of crosslinking in the processed form. The final product provides all the superior properties associated with crosslinked polyethylene. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | DIN 53479, ASTM D1505 |
| Apparent Density | 0.57 | g/cm³ | DIN 53466 |
| Melt Mass-Flow Rate (MFR) 1 | Internal method | ||
| 190°C/2.16 kg | 0.50 | g/10 min | Internal method |
| 190°C/5.0 kg | 2.2 | g/10 min | Internal method |
| Moisture Content 2 | % | Internal method | |
| Volatile Matter 3 | % | Internal method | |
| Gel Content | 69 | % | EN 579 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 24.5 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 230 | % | ISO 527-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 170 | °C | |
| Cylinder Zone 2 Temp. | 170 - 180 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Cylinder Zone 4 Temp. | 170 - 190 | °C | |
| Die Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| L/D: >25Compression ratio: 3:1 to 2.5 : 1Head: 200 to 210°CScrew: 70°C to 90 °C |
| Note Message | |
|---|---|
| 1 . | CON 2.2 |
| 2 . | CON 45.1 |
| 3 . | CON 4.3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Polyester SF 313 | Saudi Basic Industries Corporation (SABIC) | PET | SABIC® HDPE |
| Utomer UT515 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Estane® 58237 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Hytrel® SC938 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| LNP™ THERMOCOMP™ RF007SXP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |