Order Products : sales@su-jiao.com
KMI PP KM-S085J
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | KMI PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NAwDvx_KMIPPKMS085J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KM-S085J is a nucleated random copolymer for injection molding applications. This grade is designed to be processed in conventional injection molding equipment and offers high transparency, good mechanical balance, high gloss, lower cycle time, super high flow and low smell. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 11300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Distortion | 95 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PTFE 605XT X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| T & T Marketing PR-2003 Black | T & T Marketing, Inc. | Polyolefin, Unspecified | T & T Marketing |
| YUNGSOX® PP 5070 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| ASI POLYPROPYLENE PP 3369-01 | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |
| INEOS LDPE 24F564 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |