Romiloy® 1035/04 GF 10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N93ssM_Romiloy-1035-04-GF-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Romiloy®1035/04 GF 10 is a polycarbonate + acrylonitrile butadiene styrene (PC + ABS) material, and the filler is 10% glass fiber reinforced material. This product is available in Europe and is processed by extrusion or injection molding. Romiloy®The main characteristics of 1035/04 GF 10 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4220 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 71.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 4080 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 26 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 108 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 210 - 250 | °C | |
| Cylinder Zone 2 Temp. | 210 - 250 | °C | |
| Cylinder Zone 3 Temp. | 210 - 250 | °C | |
| Cylinder Zone 4 Temp. | 210 - 250 | °C | |
| Cylinder Zone 5 Temp. | 210 - 250 | °C | |
| Melt Temperature | < 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA HD-L02 PLA Impact Modifier (Transparent) | Polyvel Inc. | PLA | Polyvel PLA |
| Cawiton® MT990 | Wittenburg B.V. | SEBS | Cawiton® |
| Cleapact TI-300 | DIC Corporation | SBC | Cleapact |
| ELASTOSIL® LR 3071/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Sylvin 86052-80 Clear 8492 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |