LNP™ LUBRICOMP™ IFL36L compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N76cnR_LNP-LUBRICOMP-IFL36L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IFL-4036 LE Product reorder name: IFL36L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.44 | g/cm³ | ASTM D792 |
| -- | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9400 | MPa | ASTM D638 |
| -- | 8700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 127 | MPa | ASTM D638 |
| Break | 124 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.7 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 7910 | MPa | ASTM D790 |
| -- 5 | 7420 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 189 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 193 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 192 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.61 | ||
| vs. Itself - Static | 0.59 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.500 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 3.50 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 8 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D4812 |
| 23°C 9 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.40 | J | ASTM D3763 |
| -- | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 213 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 211 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 197 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 195 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2944-91 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nanjing Hongrui PC C1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC | Nanjing Hongrui PC |
| FERREX® GPP20CF54UL-WH | Ferro Corporation | PP, Unspecified | FERREX® |
| Hostacom SP 98/E/96 | LyondellBasell Industries | PP Copolymer | Hostacom |
| PELPRENE™ P40BU | TOYOBO America, Inc. | TPEE | PELPRENE™ |