Braskem PE HDB0358

Category:	HDPE , High Density Polyethylene
Manufacturer:	Braskem IDESA
Trademark:	Braskem PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	N72H3e_BraskemPEHDB0358.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
HDB0358 is a bimodal high-density polyethylene copolymer grade. It has an outstanding stiffness and environmental stress crack resistance (ESCR) balance making it ideal for use in a wide range of blow moulding applications. This grade is particularly well suited to chemical and detergent packaging as the exceptional ESCR can allow for significant bottle weight reduction. Application: Blow molded containers up to 25 liters capacity for packaging chemicals, many household products, oils and foodstuffs. Sheet and Corrugated Pipe Extrusion. Process: Blow Molding and Extrusion.

Message

HDB0358 is a bimodal high-density polyethylene copolymer grade. It has an outstanding stiffness and environmental stress crack resistance (ESCR) balance making it ideal for use in a wide range of blow moulding applications. This grade is particularly well suited to chemical and detergent packaging as the exceptional ESCR can allow for significant bottle weight reduction.

Application:
Blow molded containers up to 25 liters capacity for packaging chemicals, many household products, oils and foodstuffs.
Sheet and Corrugated Pipe Extrusion.

Process:
Blow Molding and Extrusion.

General Information
Features	Rigid, good High ESCR (Stress Cracking Resistance) Copolymer Bimodal molecular weight distribution
Uses	Blown Containers Packaging Bellows Blow molding applications Sheet Food packaging
Processing Method	Blow molding Pipeline extrusion molding Extrusion Sheet extrusion molding

Physical	Nominal Value	Unit	Test Method
Density	0.958	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.30	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (50°C, 100% Adinol)	> 200	hr	ASTM D1693

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	28.0	MPa	ISO 527-2
Tensile Strain (Break)	> 300	%	ISO 527-2
Flexural Modulus	1200	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength	12	kJ/m²	ISO 179

Resin Grade	Manufacturer	Category	Trademark
Softflex® 7088	Network Polymers, Inc.	TPE Alloy	Softflex®
WPP PP PPH5TF2-Natural	Washington Penn Plastic Co. Inc.	PP Homopolymer	WPP PP
Hytrel® HTR8685 BK022A	DuPont Performance Polymers	TPC-ET	Hytrel®
Innothane® IE-60A	Innovative Polymers, Inc.	TSU-Ether	Innothane®
LNP™ THERMOCOMP™ PF008S compound	SABIC Innovative Plastics	Nylon 6	LNP™ THERMOCOMP™