Purell PE 1840 H
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Purell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N4eGZI_Purell-PE-1840-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Purell PE 1840 H is a low density polyethylene with good flexibility and delivered in pellet form. It is used by our customers mainly for small blow moulding of heathcare applications such as ampoules but also be used in film applications and injection moulding. Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical (P & AD) and Business contacts first. To discuss a medical/pharmaceutical application please contact: your local Distributor or your local LyondellBasell contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shaw D | 47 | ASTM D2240 | |
| Shaw D | 45 | ISO 868 | |
| Ball Indentation Hardness (H 49/30) | 15.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% secant | 254 | MPa | ASTM D638 |
| 23°C | 200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 10.8 | MPa | ASTM D638 |
| Yield, 23°C | 9.00 | MPa | ISO 527-2 |
| Fracture | 12.2 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield | 15 | % | ISO 527-2 |
| Fracture | 670 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 241 | MPa | ASTM D790 |
| Coefficient of Friction | 0.75 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 30 to 80 µ | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 17.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (50 µm) | 120 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 87.0 | °C | ASTM D1525 |
| -- | 88.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 108 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°, 50.0 µm, Blown Film) | 75 | ASTM D523 | |
| Gloss (20°, 50.0 µm, Blown Film) | > 20 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 11 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy (50.0 µm) | 45.0 | J/cm | DIN 53373 |
| Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 180°C and a blow-up ratio of 2:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PA66 EN130 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |
| CALP 4205G-6 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Ferro PP LPP40BK80HB NATURAL | Ferro Corporation | PP, Unspecified | Ferro PP |
| Elastron® V V250.A75.B | Elastron USA, Inc. | TPV | Elastron® V |
| Generic Nylon 612 - Carbon Fiber | Generic | Nylon 612 | Generic |