Estane® 58277 TPU
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N4KO8u_Estane-58277-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Polyester Thermoplastic Polyurethane (TPU) Special Feature: Excellent Physical Properties with Good Chemical Resistance and a Wide Processing Window Processes: Extrusion: Blown, Flat Die Cast Film, Injection and Cable Jacketing |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 37.0 | mg | ASTM D3389 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (200% Strain) | 20 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 100% strain, 0.762mm | 9.70 | MPa | ASTM D412 |
| 300% strain, 0.762mm | 29.0 | MPa | ASTM D412 |
| Tensile Strength (Break, 0.762 mm) | 62.1 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 450 | % | ASTM D412 |
| Tear Strength | |||
| 0.762 mm 1 | 114 | kN/m | ASTM D624 |
| Cracking | 33 | kN/m | ASTM D470 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -20.0 | °C | ASTM D3418 |
| Melting Temperature | 130 | °C | DSC |
| Kofler Melting Temperature | 140 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze 2(1650 µm) | 1.1 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 177 | °C | |
| Cylinder Zone 2 Temp. | 182 | °C | |
| Cylinder Zone 3 Temp. | 188 | °C | |
| Cylinder Zone 4 Temp. | 193 | °C | |
| Adapter Temperature | 199 | °C | |
| Melt Temperature | 185 | °C | |
| Die Temperature | 199 | °C |
| Extrusion instructions |
|---|
| Screens: 20-40-80 meshDew Point: -40°C |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | between glass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene TPP1030 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Viton® VTR-8530 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Latamid 66 H2 G/25-V0CT1 | LATI S.p.A. | Nylon 66 | Latamid |
| INEOS HDPE K38-20-160 | INEOS Olefins & Polymers USA | MDPE | INEOS HDPE |
| SHINSTRA AG35TKB (PA6) | Shinil Chemical Industry Co., Ltd. | Nylon 6 | SHINSTRA |