LNP™ THERMOCOMP™ JF003XXZ compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N2soQn_LNP-THERMOCOMP-JF003XXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF003XXZ is a compound based on Polyethersulfone resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound JF-1003 Product reorder name: JF003XXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.67 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.51 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6210 | MPa | ASTM D638 |
| -- | 6410 | MPa | ISO 527-2/1 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 110 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.2 | % | ASTM D638 |
| Yield | 3.1 | % | ISO 527-2 |
| Fracture | 3.2 | % | ASTM D638 |
| Fracture | 3.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 5500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 176 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 670 | J/m | ASTM D4812 |
| 23°C 3 | 47 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.7 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 213 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 214 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 207 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 207 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.4E-6 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.6E-6 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 2.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 360 - 371 | °C | |
| Front Temperature | 371 - 382 | °C | |
| Processing (Melt) Temp | 354 - 371 | °C | |
| Mold Temperature | 138 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2925-75 Clear 8392 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Cardia Biohybrid™ H-FM | Cardia Bioplastics™ | TPS+PP | Cardia Biohybrid™ |
| PolyBlend™ 1100 75A | CardioTech International, Inc. | PUR, Unspecified | PolyBlend™ |
| ALTECH® PC ECO 1000/578 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| Sylvin 9769-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |