Devcon High Performance Backing Compound
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N14hhc_Devcon-High-Performance-Backing-Compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High-strength liquid epoxy with the necessary resiliency and strength to withstand forces generated by crushers and mills. Intended Use:
Product Features:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | |
| Specific Volume | 0.621 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | 121 | °C | |
| Tensile Shear Adhesion | 7.58 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.060 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6550 | MPa | ASTM D638 |
| Tensile Strength | 53.0 | MPa | ASTM D638 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Compressive Strength | 130 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 69.4 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100 Mixing ratio by capacity: 10 | ||
| Component B | Mixing ratio by weight: 5.9 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 56 | min | |
| Thermoset Mix Viscosity | 10300 | cP |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 8.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenogel® ABS A3 HS PRTA010 AB330 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| Complet® LCF30-PES | PlastiComp, Inc. | PESU | Complet® |
| Hostaform® C 9021 LS 10/1570 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Hylon® N1020L | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| INSPIRE™ 6025 | Braskem America Inc. | PP Homopolymer | INSPIRE™ |