Halene L 92001W
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N0yCKd_Halene-L-92001W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
92001W is a 1-Hexene LLDPE copolymer blown film grade produced by the Spherilene Technology. This grade can be used in Adhesive Lamination Film Applications. 92001W is without Slip and Antiblocking additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested 2 | 55 | µm | |
| Tensile Strength 3 | ASTM D882 | ||
| MD : Yield, 55 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 55 µm | 10.0 | MPa | ASTM D882 |
| MD : Break, 55 µm | 31.0 | MPa | ASTM D882 |
| TD : Break, 55 µm | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 55 µm | 950 | % | ASTM D882 |
| TD : Break, 55 µm | 1100 | % | ASTM D882 |
| Dart Drop Impact 4 | 280 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 55 µm | 550 | g | ASTM D1922 |
| TD : 55 µm | 800 | g | ASTM D1922 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 80 | ASTM D2457 |
| Additional Information |
|---|
| Barrel Temperature: 180 - 200 °CBlow up Ratio: 2.0 - 3.0Die Gap: 2.0 - 2.5 mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | BUR - 2.5, Die Gap - 2.5 mm |
| 3 . | 500 mm/min |
| 4 . | F50, 38 mm Dart, 66-cm. Height |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 504 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Ateva® 1850A | Celanese EVA Performance Polymers | EVA | Ateva® |
| Filter-bond™ E-3264 | Hapco Inc. | TS, Unspecified | Filter-bond™ |
| Gallonprene® GP210-5502L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LNP™ LUBRICOMP™ AG5LT2 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |