Ultramid® C3U Datasheet,Nylon 66/6,BASF Corporation-SHANGHAI SUSHENG

Message
Ultramid C3U is an injection molding, general purpose PA6/66 grade with improved flame retardance. The product is UL recognized as 94V0 at 0.4 mm minimum thickness. Applications It is used for impact resistant electrical insulating parts such as contact bases and plug connector strips.

General Information
Features	Flame Retardant General Purpose Good Impact Resistance
Uses	Electrical Parts Electronic Insulation General Purpose
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.16	--	g/cm³	ASTM D792, ISO 1183
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)	140	--	cm³/10min	ISO 1133
Molding Shrinkage - Flow (3.18 mm)	0.80	--	%
Water Absorption
Saturation	8.5	--	%	ASTM D570
Saturation, 23°C	8.5	--	%	ISO 62
Equilibrium, 50% RH	2.9	--	%	ASTM D570
Equilibrium, 23°C, 50% RH	2.9	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	100	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	3500	1500	MPa	ISO 527-2
Tensile Strength
Yield, 23°C	83.0	--	MPa	ASTM D638
Yield, 23°C	75.0	45.0	MPa	ISO 527-2
Tensile Elongation
Yield, 23°C	5.0	--	%	ASTM D638
Yield, 23°C	4.0	18	%	ISO 527-2
Break, 23°C	50	--	%	ASTM D638
Nominal Tensile Strain at Break (23°C)	6.0	> 50	%	ISO 527-2
Flexural Modulus (23°C)	3000	--	MPa	ASTM D790, ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179
-30°C	4.0	--	kJ/m²
23°C	9.0	35	kJ/m²
Charpy Unnotched Impact Strength (23°C)	80 kJ/m²	No Break		ISO 179
Notched Izod Impact
-40°C	32	--	J/m	ASTM D256
23°C	43	--	J/m	ASTM D256
23°C	4.5	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	224	--	°C	ASTM D648
1.8 MPa, Unannealed	91.0	--	°C	ASTM D648
1.8 MPa, Unannealed	70.0	--	°C	ISO 75-2/A
Peak Melting Temperature	243	--	°C	ASTM D3418, ISO 3146
CLTE
Flow	4.0E-5	--	cm/cm/°C	ASTM E831
Flow	8.0E-5	--	cm/cm/°C
Transverse	9.0E-5	--	cm/cm/°C
RTI Elec				UL 746
0.380 mm	110	--	°C
0.750 mm	120	--	°C
1.50 mm	120	--	°C
3.00 mm	120	--	°C
RTI Imp				UL 746
0.380 mm	65.0	--	°C
0.750 mm	105	--	°C
1.50 mm	105	--	°C
3.00 mm	105	--	°C
RTI Str				UL 746
0.380 mm	65.0	--	°C
0.750 mm	115	--	°C
1.50 mm	120	--	°C
3.00 mm	120	--	°C

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity
1.50 mm	1.0E+13	1.0E+9	ohms·cm	ASTM D257
--	1.0E+13	1.0E+9	ohms·cm	IEC 60093
Electric Strength	32	28	kV/mm	IEC 60243-1
Dielectric Constant (1 MHz)	3.60	6.00		IEC 60250
Dissipation Factor (1 MHz)	0.020	0.30		IEC 60250
Comparative Tracking Index	600	600	V	IEC 60112

Flammability	Dry	Conditioned	Test Method
Flame Rating			UL 94
0.380 mm	V-0	--
0.750 mm	V-0	--
1.50 mm	V-0	--
3.00 mm	V-0	--

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	BASF Corporation
Trademark:	Ultramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	N0oKkY_Ultramid-C3U.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TEREZ PA 6.6 7500 GF 25 FL HF/2	TER HELL PLASTIC GMBH	Nylon 66	TEREZ PA 6.6
NaturePlast PLI 013	NaturePlast	PLA	NaturePlast
DEXFLEX® 1011E	LyondellBasell Industries	TPO (POE)	DEXFLEX®
Generic PPE+PS - Glass\Mineral	Generic	PPE+PS	Generic
Durethan® BKV 30 H2.0 000000	LANXESS GmbH	Nylon 6	Durethan®