EXTEM™ XH1005 resin
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | EXTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | N00NLG_EXTEMXH1005resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Heat Amorphous TPI Blend, Tg 267C, High Continuous Use Temperature (CUT), Excellent FR, OSU and LOI. Material is UL listed. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Resin is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited. Also UL rated 94V0 at 1.3mm and 3.0mm. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (367°C/6.6 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 1.2 | % | Internal method |
| Water Absorption | |||
| 23°C, 24 hr 1 | 0.60 | % | ASTM D570 |
| Saturated, 23°C | 2.3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3420 | MPa | ASTM D638 |
| -- | 3160 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 103 | MPa | ASTM D638 |
| Yield | 101 | MPa | ISO 527-2/5 |
| Fracture 4 | 96.0 | MPa | ASTM D638 |
| Fracture | 70.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Fracture 6 | 15 | % | ASTM D638 |
| Fracture | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 7 | 3130 | MPa | ASTM D790 |
| -- 8 | 2850 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 168 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 21 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 11 | 4.4 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 20.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 250 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 235 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 237 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 225 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 260 | °C | ASTM D1525 13 |
| -- | 253 | °C | ISO 306/B50 |
| -- | 252 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 5.1E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.75 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 175 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 70 | % | |
| Rear Temperature | 360 - 385 | °C | |
| Middle Temperature | 370 - 400 | °C | |
| Front Temperature | 380 - 410 | °C | |
| Nozzle Temperature | 375 - 405 | °C | |
| Processing (Melt) Temp | 380 - 410 | °C | |
| Mold Temperature | 150 - 175 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 70 - 100 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Results measured at 48 hrs |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4582 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Moplen RP346R | HMC Polymers | PP Random Copolymer | Moplen |
| Zytel® 101F NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Bayflex® 110-80 (15% Glass) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Ebalta LH 26 / Resin+Hardener | Ebalta Kunststoff GmbH | Epoxy | Ebalta |